Températures de fléchissement sous charge - TFC (Heat Distorsion Temperatures - HDT) de polymères
| Polymère |
TFC (HDT) en °C Méthode A (1,8 MPa) |
|
ABS
|
95-100
|
|
CA
|
43
|
|
CAB
|
42
|
|
CP
|
37
|
|
ETFE
|
70-100
|
|
MABS
|
90
|
|
PA-11
|
52
|
|
PA-12
|
50
|
|
PA-4,6
|
160
|
|
PA-6
|
77-80
|
|
PA-6,12
|
166
|
|
PA-6,6
|
77
|
|
PAEK
|
170
|
|
PAI
|
278
|
|
PBT
|
65-67
|
|
PC
|
128-135
|
|
PE UHMW
|
40-50
|
|
PEbd
|
30-40
|
|
PEEK
|
152
|
|
PEhd
|
42-50
|
|
PEI
|
200
|
|
PEP
|
70
|
|
PESU
|
195
|
|
PET AMORPHE
|
65
|
|
PF2C1
|
160
|
|
PF2D1
|
130
|
|
PF2D4
|
125
|
|
PF2E1
|
160-200
|
|
PMMA
|
70-90
|
|
POM
|
110-115
|
|
PP
|
45
|
|
PP + 40% Mica
|
100
|
|
PP + 40% Talc
|
85
|
|
PPA
|
120
|
|
PPE
|
110-130
|
|
PPSU
|
207
|
|
PS CHOC
|
70-86
|
|
PS CRISTAL
|
70-90
|
|
PS CRISTAL 1540 non recuit (TOTAL)
|
73
|
|
PS CRISTAL 1540 recuit (TOTAL)
|
83
|
|
PSU
|
165-170
|
|
PTFE
|
50
|
|
PVC Rigide
|
60-75
|
|
PVCC
|
95-105
|
|
PVDC
|
80-90
|
|
PVDF
|
110-115
|
|
SAN
|
90-105
|